API 5L X42 PSL 1

API 5L X42 PSL 1

API 5L X42 PSL 1 Line Pipes, API 5L X42 PSL 1 Carbon Steel Line Pipes Manufacturer, Exporter & Suppliers.

API 5L X42 PSL 1 Seamless Pipes, API 5L X42 PSL 1 Welded Pipes, ERW Pipes Suppliers in India.

API 5L X42 PSL 1

Pragati Metal Corporation is leading Manufacturers, Supplier and Exporters of high quality API 5L X42 PSL 1 Pipes. We manufacture these Seamless Steel Pipes using extreme grade of raw material which is procured. With the varied thickness and other dimensional specifications these are offered in seamless and welded. All products are industry-standard conforming to or exceeding API, ASTM, ASME, ANSI and other national and international standards. We offer these pipes in different dimentions, shapes, sizes, material specifications as per clients own requirement.

Specification :
Sizes (Seamless) : 1/2” NB – 60” NB
Sizes (ERW) : 1/2” NB – 24” NB
Sizes (SAW) : 16” NB – 100” NB
Sizes LSAW/DSAW : 16’OD TO 54′ OD (8 MM TO 50 MM THK)
Wall Thickness : SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness
Dimensions : All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API.
Additional Testing : NACE MR0175, NACE TM0177, NACE TM0284, HIC TEST, SSC TEST, H2 SERVICE, IBR, etc.
Chemical Composition :
Mass fraction, based upon heat and product analysis a
SEAMLESS PIPE
C Mn P V Nb Ti
maxb maxb max. max. max. max. max.
0.28 1.20 0.030 0.030 c,d c,d d
WELDED PIPE
0.26 1.20 0.030 0.030 c,d c,d d
Mechanical properties
Y.S T.S ELONGATION
Mpa(psi) Mpa(psi)
min min min
245(35 500) 415(60 200) 28%

• 0.50% maximum for copper, 0.50% maximum for nickel, 0.50% maximum for chromium, and 0.15% maximum for molybdenum.
• For each reduction of 0.01% below the specified maximum concetration for carbon, an increase of 0.05% above the specified maximum    concentration for manganese is permissible, up to a maximum of 1.65%
• Unless otherwise agreed, the sum of the niobium and vanadium contents shall be ≤0.06%.
• The sum of the niobium ,vanadium and titanium concentratons shall be ≤0.06%.
• Unless otheriwse agreed.
• Unless otherwise agreed, the sum of niobium, vanadium and titanium concentrations shall be ≤ 0.15%