API 5L X52 PSL 1

API 5L X52 PSL 1

API 5L X52 PSL 1 Line Pipes, API 5L X52 PSL 1 Carbon Steel Line Pipes Manufacturer, Exporter & Suppliers.

API 5L X52 PSL 1 Seamless Pipes, API 5L X52 PSL 1 Welded Pipes, ERW Pipes Suppliers in India.

API 5L X52 PSL 1

We are also Manufacturers, Supplier and Exporters of API 5L X52 PSL 1 Pipes. These are used for building construction and industries like oil, petrochemical, refinery and many more. We also offer competitive pricing on small & larger quantity. These are available in various quality attributes. We offer these pipes in different dimentions, shapes, sizes, material specifications as per clients own requirement.

Specification :
Sizes (Seamless) : 1/2” NB – 60” NB
Sizes (ERW) : 1/2” NB – 24” NB
Sizes (SAW) : 16” NB – 100” NB
Sizes LSAW/DSAW : 16’OD TO 54′ OD (8 MM TO 50 MM THK)
Wall Thickness : SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness
Dimensions : All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API.
Additional Testing : NACE MR0175, NACE TM0177, NACE TM0284, HIC TEST, SSC TEST, H2 SERVICE, IBR, etc.
Chemical Composition :
Mass fraction, based upon heat and product analysis a
SEAMLESS PIPE
C Mn P V Nb Ti
maxb maxb max. max. max. max. max.
0.28 1.20 0.030 0.030 c,d c,d d
WELDED PIPE
0.26 1.20 0.030 0.030 c,d c,d d
Mechanical properties
Y.S T.S ELONGATION
Mpa(psi) Mpa(psi)
min min min
360 (52 200) 460 (66 700) 28%

• 0.50% maximum for copper, 0.50% maximum for nickel, 0.50% maximum for chromium, and 0.15% maximum for molybdenum.
• For each reduction of 0.01% below the specified maximum concetration for carbon, an increase of 0.05% above the specified maximum    concentration for manganese is permissible, up to a maximum of 1.65%
• Unless otherwise agreed, the sum of the niobium and vanadium contents shall be ≤0.06%.
• The sum of the niobium ,vanadium and titanium concentratons shall be ≤0.06%.
• Unless otheriwse agreed.
• Unless otherwise agreed, the sum of niobium, vanadium and titanium concentrations shall be ≤ 0.15%